l One-componenthigh thixotropic silica gel, this product has good adhesion and moderatestrength;
l It can be used alone or in combination with fluorescent powder for strippackaging, and will not collapse after high temperature at high temperature;
l Stable opticalperformance and low light decay, improving light efficiency;
l After curing, it can pass aging test such as cold and heat cycle impact,reflow soldering test, UV test;
l Various three-dimensional shapes can be drawnby the dispenser to obtain various illumination angles, which are often usedfor the packaging of rigid LED filament bulbs.
|
inspecting item
|
Unit / test method
|
numerical value
|
|
surface
|
——
|
Translucent colloid
|
|
dynamic viscosity
|
MPa·s/(25℃，10rpm)
|
30-50
|
|
Tectonic viscosity ratio
|
/(3rpm/30rpm)
|
>3
|
|
condition of cure
|
℃/h
|
170℃/4h
|
|
Gel Time
|
sec./(150℃)
|
15
|
|
Operating time at room temperature
|
hrs./(25℃)
|
24
|
|
storage time
|
months./(-10℃-10℃)
|
3
|
|
refractive index
|
/(25℃)
|
1.41
|
|
density
|
G/cm3
|
1.05
|
|
hardness
|
Shore A
|
50
|
|
shear strength
|
MPa
|
>3
|
|
tensile strength
|
MPa
|
>4
|
|
mass resistivity
|
Ω·cm/(25℃)
|
>1015
|
|
coefficient of linear expansion
|
ppm/℃(α2)
|
21
|
l One-componenthigh thixotropic silica gel, this product has good adhesion and moderatestrength;
l It can be usedalone or in combination with fluorescent powder for strip packaging, and willnot collapse after high temperature at high temperature;
l Stable opticalperformance and low light decay, improving light efficiency;
l After curing,it can pass aging test such as cold and heat cycle impact, reflow solderingtest, UV test;
l Variousthree-dimensional shapes can be drawn by the dispenser to obtain variousillumination angles, which are often used for the packaging of rigid LEDfilament bulbs.
|
inspecting item
|
Unit / test method
|
numerical value
|
|
surface
|
——
|
Translucent colloid
|
|
dynamic viscosity
|
MPa·s/(25℃，10rpm)
|
25-35
|
|
Tectonic viscosity ratio
|
/(3rpm/30rpm)
|
>3
|
|
condition of cure
|
℃/h
|
170℃/4h
|
|
Gel Time
|
sec./(150℃)
|
15
|
|
Operating time at room temperature
|
hrs./(25℃)
|
24
|
|
storage time
|
months./(-10℃-10℃)
|
3
|
|
refractive index
|
/(25℃)
|
1.41
|
|
density
|
G/cm3
|
1.05
|
|
hardness
|
Shore A
|
50
|
|
shear strength
|
MPa
|
>3
|
|
tensile strength
|
MPa
|
>4
|
|
mass resistivity
|
Ω·cm/(25℃)
|
>1015
|
|
coefficient of linear expansion
|
ppm/℃(α2)
|
210
|
l Two-componenthigh thixotropic silicone, this product has good adhesion and moderate strength;
l It can be usedalone or in combination with fluorescent powder for strip packaging, and willnot collapse after high temperature at high temperature;
l Stable opticalperformance and low light decay, improving light efficiency;
l After curing,it can pass aging test such as cold and heat cycle impact, reflow solderingtest, UV test;
l Variousthree-dimensional shapes can be drawn by the dispenser to obtain variousillumination angles, which are often used for the packaging of rigid LEDfilament bulbs.
|
inspecting item
|
Unit / test method
|
numerical value
|
|
surface
|
——
|
Agent A translucent colloid B clear liquid.
|
|
dynamic viscosity
|
MPa·s/(25℃，10rpm)
|
30-50
|
|
Tectonic viscosity ratio
|
/(3rpm/30rpm)
|
>3
|
|
condition of cure
|
℃/h
|
170℃/4h
|
|
Gel Time
|
sec./(150℃)
|
15
|
|
Operating time at room temperature
|
hrs./(25℃)
|
24
|
|
storage time
|
months./(-10℃-10℃)
|
6
|
|
refractive index
|
/(25℃)
|
1.41
|
|
density
|
G/cm3
|
1.05
|
|
hardness
|
Shore A
|
50-55
|
|
light transmittance
|
-
|
＞85%
|
|
tensile strength
|
MPa
|
>4
|
|
mass resistivity
|
Ω·cm/(25℃)
|
>1015
|
|
coefficient of linear expansion
|
ppm/℃(α2)
|
210
|
l Two-componenthigh thixotropic silicone, this product has good adhesion and moderate strength;
l It can be usedalone or in combination with fluorescent powder for strip packaging, and willnot collapse after high temperature at high temperature;
l Stable opticalperformance and low light decay, improving light efficiency;
l After curing,it can pass aging test such as cold and heat cycle impact, reflow solderingtest, UV test;
l A variety ofthree-dimensional shapes can be drawn by the dispenser, and variousillumination angles are obtained, which are commonly used for packaging ofhigh-power LED filament bulbs of 15 mA or more.
|
inspecting item
|
Unit / test method
|
numerical value
|
|
surface
|
——
|
Agent A translucent colloid B clear liquid.
|
|
dynamic viscosity
|
MPa·s/(25℃，10rpm)
|
30-50
|
|
Tectonic viscosity ratio
|
/(3rpm/30rpm)
|
>3
|
|
condition of cure
|
℃/h
|
170℃/4h
|
|
Gel Time
|
sec./(150℃)
|
15
|
|
Operating time at room temperature
|
hrs./(25℃)
|
24
|
|
storage time
|
months./(-10℃-10℃)
|
6
|
|
refractive index
|
/(25℃)
|
1.41
|
|
density
|
G/cm3
|
1.05
|
|
hardness
|
Shore A
|
50-55
|
|
light transmittance
|
-
|
＞85%
|
|
tensile strength
|
MPa
|
>4
|
|
mass resistivity
|
Ω·cm/(25℃)
|
>1015
|
|
coefficient of linear expansion
|
ppm/℃(α2)
|
210
|
l Two-component addition molding silicone potting glue, mainly suitablefor integral molding of LED point light source;
l Moderateviscosity, good formability, easy to inject
l Fast curing, goodadhesion, smooth, full and non-collapse after curing;
l Excellent heat resistance, long-termresistance to high temperatures above 260 °C, no cracking, nohardening and no yellowing.
|
project
|
technical parameter
|
|
Before curing
(component A)
|
surface
|
Translucent liquid
|
|
dynamic viscosity
mPa·s（25℃）
|
50000 - 60000
|
|
Before curing
(component B)
|
surface
|
transparency liquid
|
|
dynamic viscosity
mPa·s（25℃）
|
300 - 500
|
|
Usage scale
|
4：1
|
|
post-mixed viscosity mPa·s（25℃）
|
10000 -15000
|
|
typical curing conditions
|
150℃×2h
|
|
after curing
|
surface
|
Colorless transparent elastic body
|
|
hardness（ShoreA）
|
45 ± 5
|
|
refractive index (25℃ )
|
1.41
|
|
light transmittance
(% 、1mm@450nm)
|
>85
|